The glass transition temperature and the crystallinity of the composites were examined using the DSC module Q2000 from TA Instruments (New Castle, USA). The granules were heated from 0 °C to 250 °C at a heating rate of 10 K/min, cooled down and heated up again. The second heating cycle was used to evaluate irreversible changes in crystallinity and glass transition temperature.